Chemical Stability Research Articles

Chemical stability of β-carotene composite or bilayer emulsions coated with pea protein isolate and γ-polyglutamic acid compared to monolayer emulsion

Abstract The integration of β-carotene into functional foods is limited due to its limited hydrophilicity and chemical stability. To address this issue, emulsion was encouraged to be utilized. Monolayer, composite, and bilayer emulsions were prepared using pea protein isolate (PPI) alone or in combination with poly-γ-glutamic acid (γ-PGA). Our findings indicate that the bilayer emulsion utilizing γ-PGA as an external emulsifier exhibited the smallest droplet size (737.61 nm) and highest zeta potential (−35.23 mV). Under various environmental stresses, the chemical stability of the composite emulsion surpassed that of the monolayer emulsion but was inferior to that of the bilayer emulsion. Moreover, following simulated gastrointestinal digestion, the β-carotene bioaccessibility in the composite emulsion (12.76 %) exceeded that in the monolayer emulsion (6.57 %) but was less than that in the bilayer emulsion (20.01 %). Therefore, the emulsion preparation method or the sequence of γ-PGA addition significantly affects emulsion stability. Among the studied emulsions, the bilayer emulsion demonstrated the most stable structure, enhancing the stability of β-carotene within the oil droplets.

Square-planar Tetranuclear Cluster-based Alkaline Earth Metal-organic Frameworks with Enhanced Proton Conductivity.

Alkaline earth (AE) metal complexes have garnered significant interest in various functional fields due to their nontoxicity, low density, and low cost. However, there is a lack of systematic investigation into the structural characteristics and physical properties of AE-metal-organic frameworks (MOFs). In this research, we synthesized isostructural MOFs consisting of AE4(μ4-Cl) clusters bridged by benzo-(1,2;3,4;5,6)-tris(thiophene-2'-carboxylic acid) (BTTC3-) ligands. The resulting structure forms a truncated octahedral cage denoted as [AE4(m4-Cl)]6(BTTC)8, which further linked to a porous three-dimensional framework. Among the investigated AE ions (Ca, Sr, and Ba), the Ca4-MOF demonstrated good chemical stability in water compared to Sr4-MOF and Ba4-MOF. The N2 adsorption and solid-state UV-vis-NIR absorption behaviors were evaluated for all AE4-MOFs, showing similar trends among the different metal ions. Additionally, the proton conduction study revealed that the Ca4-MOF exhibited ultra-high proton conductivity, reaching 3.52×10-2 S cm-1 at 343 K and 98 % RH. Notably, the introduction of LiCl via guest exchange resulted in an improved proton conduction of up to 6.36×10-2 S cm-1 under similar conditions in the modified LiCl@Ca4-MOF. The findings shed light on the regulation of physical properties and proton conductivity of AE-MOFs, providing valuable insights for their potential applications in various fields.

One-dimensional photonic crystals based on porous anodic alumina: Optical and morphology changes under thermal and chemical treatments

One-dimensional photonic crystals (1D PCs) based on porous anodic aluminium oxide (AAO) are promising for light manipulation and sensing. As-prepared AAO, being amorphous material, suffers degradation in acidic and alkaline media. It is commonly known that the chemical stability of AAO increases drastically after thermal treatment. Here, the effect of annealing up to 1200 °C on the morphology and the optical properties of AAO PCs is studied. The two-step crystallization of as-prepared AAO at 860 and 1190 °C leads to a two-step blue shift of the central wavelength of photonic band gap (PBG) and the decrease in PBG depth, whereas the Q-factor of the PBG enhances. The observed changes in optical transmittance spectra of PCs are mainly attributed to the increase in pore diameter, the formation of crystalline particles of alumina polymorphs, and the removal of impurities. Annealed AAO PCs demonstrate much higher stability of optical parameters during exposure in acidic media compared to the as-prepared ones. Thermal treatment at 600 °C results in 30% decrease in the rate of the PBG shift during chemical etching. Furthermore, AAO crystallization into a mixture of low-temperature alumina polymorphs at 860 °C leads in a negligible change in transmittance spectra even after chemical etching in 1 M HCl for 75 h. The excellent stability achieved for the annealed AAO PCs in aggressive media proves the perspectives of their application as the optical sensors with long-term stability.

Highly sensitive and selective fluorescent "turn-on" sensor for Ag+ detection using MAPbBr3@PCN-221(Fe): An efficient Ag+-bridged energy transfer from perovskite to MOF.

Metal ion-induced water pollution is attracting increasing public attention. Perovskite quantum dots and metal-organic frameworks (MOFs), owing to their outstanding properties, hold promise as ideal probes for detecting metal ions. In this study, a composite material, MAPbBr3@PCN-221(Fe), was prepared by encapsulating MAPbBr3 quantum dots with PCN-221(Fe), demonstrating high chemical stability and good reusability. The composite material shows a sensitive fluorescence turn-on signal in the presence of silver ions. The fluorescence intensity of the composite material exhibits a linear relationship with the concentration of Ag+ in the solution, with a low detection limit of 8.68 µM. Moreover, the fluorescence signal exhibits a strong selectivity for Ag+, enabling the detection of Ag+ concentration. This fluorescence turn-on signal originates from the Ag+-bridged energy transfer from the conductive band of MAPbBr3 to the excited state of the MOF, which is directly proportional to the concentration of silver ions. Simultaneously, this finding may open up a new possibility in artificial controlled energy transfer from perovskite to MOF for future development.

Crystal orientation of epitaxial film deposited on silicon surface

Direct growth of oxide film on silicon is usually prevented by extensive diffusion or chemical reaction between silicon (Si) and oxide materials. Thermodynamic stability of binary oxides is comprehensively investigated on Si substrates and shows possibility of chemical reaction of oxide materials on Si surface. However, the thermodynamic stability does not include any crystallographic factors, which is required for epitaxial growth. Adsorption energy evaluated by total energy estimated with the density functional theory predicted the orientation of epitaxial film growth on Si surface. For lower computing cost, the adsorption energy was estimated without any structural optimization (simple total of energy method). Although the adsorption energies were different on simple ToE method, the crystal orientation of epitaxial growth showed the same direction with/without the structural optimization. The results were agreed with previous simulations including structural optimization. Magnesium oxide (MgO), as example of epitaxial film, was experimentally deposited on Si substrates and compared with the results from the adsorption evaluation. X-ray diffraction showed cubic on cubic growth [MgO(100)//Si(100) and MgO(001)//Si(001)] which agreed with the results of the adsorption energy.

Deep mutational scanning reveals a correlation between degradation and toxicity of thousands of aspartoacylase variants

Unstable proteins are prone to form non-native interactions with other proteins and thereby may become toxic. To mitigate this, destabilized proteins are targeted by the protein quality control network. Here we present systematic studies of the cytosolic aspartoacylase, ASPA, where variants are linked to Canavan disease, a lethal neurological disorder. We determine the abundance of 6152 of the 6260 ( ~ 98%) possible single amino acid substitutions and nonsense ASPA variants in human cells. Most low abundance variants are degraded through the ubiquitin-proteasome pathway and become toxic upon prolonged expression. The data correlates with predicted changes in thermodynamic stability, evolutionary conservation, and separate disease-linked variants from benign variants. Mapping of degradation signals (degrons) shows that these are often buried and the C-terminal region functions as a degron. The data can be used to interpret Canavan disease variants and provide insight into the relationship between protein stability, degradation and cell fitness.

Synthesis, optical characterization and electrical behavior of chitosan/MgO/Cr2O3 nanocomposite for electrical applications

Magnesium oxide nanoparticles (MgO NPs) are straightforward, cheap, biocompatible, and biodegradable, making them one of the most popular inexpensive and non-toxic nanoparticles. In addition, Nanosized chromic oxide (Cr2O3) is a significant transition metal oxide due to its numerous exceptional attributes, it finds application in several domains. It has good electrical conductivity, excellent thermal and chemical stability. It is utilized in several industries for its ability to resist oxidation at high temperatures, as well as its application in refractory materials and catalysts. In this study, we utilized a laser ablation approach to synthesize a ternary nanocomposite composed of MgO and Cr2O3 nanoparticles as it is considered a clean method for the preparation of nanoparticles. Subsequently, these nanoparticles were integrated into Chitosan (CS) solution to create polymer nanocomposite via casting route. XRD confirmed the formation of Cr2O3 nanocrystals with size of 61 nm dispersed in chitosan/MgO matrix. FTIR verified the interactions between chitosan, MgO, and Cr2O3 nanoparticles. The broadening and shifting of the OH and NH bands with increasing Cr2O3 content confirms the interaction and complexation between Cr2O3 and Chitosan/MgO. UV–Vis analysis revealed that incorporating 7 wt% Cr2O3 reduced optical band gap from 5.59 eV for chitosan to 3.91 eV. The band gap values decreased with increasing Cr2O3 content due to polaronic defects. TGA showed improved thermal stability, with the 7 wt% Cr2O3 nanocomposite exhibiting a residual mass of 47 % at 700 °C compared to 28 % for chitosan. Dielectric studies demonstrated high dielectric constant and conductivity (10−5 S/cm at 10 Hz) values for the 7 wt% Cr2O3 nanocomposite, attributed to interfacial polarization effects and nanocapacitor formation by the conductive nanofillers. The ternary chitosan/MgO/Cr2O3 nanocomposites with tunable optical, thermal and electrical properties show promising potential for electronic applications.

Magnetic domain structures in ultrathin Bi2Te3/CrTe2 heterostructures

Abstract Chromium tellurium compounds are important two-dimensional van der Waals ferromagnetic materials with high Curie temperature and chemical stability in air, which is promising for applications in spintronic devices. Here, high-quality spin-orbital-torque (SOT) device, Bi2Te3/CrTe2 heterostructure was epitaxially grown on Al2O3 (0001) substrates. Anomalous Hall measurements indicate the existence of strong ferromagnetism in this device with the CrTe2 thickness down to 10 nm. In order to investigate its micromagnetic structure, cryogenic magnetic force microscope (MFM) was utilized to measure the magnetic domain evolutions at various temperatures and magnetic fields. The virgin domain state of the device shows a worm-like magnetic domain structure with the size around 0.6 ~ 0.8 µm. Larger irregular-shape magnetic domains (＞1µm) can be induced and pinned, after the field is increased to coercive field and ramped back to low fields. The temperature-dependent MFM signals exhibit a nice mean-field-like ferromagnetic transition with Curie temperature around 201.5 K, indicating a robust ferromagnetic ordering. Such device can be potentially implemented in future magnetic memory technology.

Interlayer Potassium Single-Atom-Coordinated g-C3N4 for Significantly Boosted Visible Light Photocatalytic H2 Production.

In recent years, graphitic carbon nitride (g-C3N4) has attracted considerable attention because it includes earth-abundant carbon and nitrogen elements and exhibits good chemical and thermal stability owing to the strong covalent interaction in its conjugated layer structure. However, bulk g-C3N4 has some disadvantages of low specific surface area, poor light absorption, rapid recombination of photogenerated charge carriers, and insufficient active sites, which hinder its practical applications. In this study, we design and synthesize potassium single-atom (K SAs)-doped g-C3N4 porous nanosheets (CM-KX, where X represents the mass of KHP added) via supramolecular self-assembling and chemical cross-linking copolymerization strategies. The results show that the utilization of supramolecules as precursors can produce g-C3N4 nanosheets with reduced thickness, increased surface area, and abundant mesopores. In addition, the intercalation of K atoms within the g-C3N4 nitrogen pots through the formation of K-N bonds results in the reduction of the band gap and expansion of the visible-light absorption range. The optimized K-doped CM-K12 nanosheets achieve a specific surface area of 127 m2 g-1, which is 11.4 times larger than that of the pristine g-C3N4 nanosheets. Furthermore, the optimal CM-K12 sample exhibits the maximum H2 production rate of 127.78 μmol h-1 under visible light (λ ≥ 420 nm), which is nearly 23 times higher than that of bare g-C3N4. This significant improvement of photocatalytic activity is attributed to the synergistic effects of the mesoporous structure and K SAs doping, which effectively increase the specific surface area, improve the visible-light absorption capacity, and facilitate the separation and transfer of photogenerated electron-hole pairs. Besides, the optimal sample shows good chemical stability for 20 h in the recycling experiments. Density functional theory calculations confirm that the introduction of K SAs significantly boosts the adsorption energy for water and decreases the activation energy barrier for the reduction of water to hydrogen.

Smartphone-Integrated Automated Sensor Employing Electrochemically Engineered 3D Bimetallic Nanoflowers for Hydrogen Peroxide Quantification in Milk.

Hydrogen peroxide (H2O2), one of the reactive oxygen species in living beings, serves as a regulator of various cellular processes. However, excessive peroxide concentrations are linked to oxidative stress and promptly disrupt cellular components, leading to several pathological conditions in the body. Moreover, it is extremely reactive and has a limited lifetime; thus, H2O2 sensing remains a prominent focus of research. Enzymatic sensing probes were widely employed to detect H2O2 in the recent past; however, they are susceptible to intrinsic chemical and thermal instabilities, which decrease the reliability and durability of the surface. This research was designed to come up with a feasible solution to this problem. Herein, a novel nonenzymatic peroxidase-mimic three-dimensional (3D) bimetallic nanoflower has been synergistically engineered for quick sensing of H2O2. The sensor platform showed minimal resistance or enhanced charge transfer properties as well as remarkable analytical capability, having a broad linear range between 0.01 and 1 nM and a detection limit of 1.46 ± 0.07 pM. The probe responded to changes in H2O2 concentration in just 2.10 ± 0.02 s, making it a quick sensing platform for H2O2 tracking. This peroxidase-mimic nanozyme probe showed minimal sensitivity to interferants often seen in real-world sample matrices and possessed good recoveries ranging from 92.88 to 99.09% in milk samples. Further, a facile and user-friendly smartphone application (APP) named "HPeroxide-Check" was developed and integrated into the sensor to check the milk adulteration by detecting H2O2. It processes the current output obtained from the sensing interface and provides real-time peroxide concentrations in milk. The entire procedure of fabricating the probe is a single, highly robust step that takes only 10 min and is coupled with a smartphone APP, highlighting the sensor's quick manufacturing and deployment for automated H2O2 monitoring in industrial and point-of-care settings.

Design and Development of a Polymeric-Based Curcumin Nanoparticle for Drug Delivery Enhancement and Potential Incorporation into Nerve Conduits

Peripheral nerve injuries (PNI) impact millions of individuals in the United States, prompting thousands of nerve repair procedures annually. Nerve conduits (NC) are commonly utilized to treat nerve injuries under 3 cm but larger gaps still pose a challenge for successful peripheral nerve regeneration (PNR) and functional recovery. This is partly attributed to the absence of bioactive agents such as stem cells or growth factors in FDA-approved conduits due to safety, harvesting, and reproducibility concerns. Therefore, curcumin, a bioactive phytochemical, has emerged as a promising alternative bioactive agent due to its ability to enhance PNR and overcome said challenges. However, its hydrophobicity and rapid degradation in aqueous solutions are considerable limitations. In this work, a nanoscale delivery platform with tannic acid (TA) and polyvinylpyrrolidone (PVP) was developed to encapsulate curcumin for increased colloidal and chemical stability. The curcumin nanoparticles (CurNPs) demonstrate significantly improved stability in water, reduced degradation rates, and controlled release kinetics when compared to free curcumin. Further, cell studies show that the CurNP is biocompatible when introduced to neuronal cells (SH-SY5Y), rat Schwann cells (RSC-S16), and murine macrophages (J774 A.1) at 5 μM, 5 μM, and 10 μM of curcumin, respectively. As a result of these improved physicochemical properties, confocal fluorescence microscopy revealed superior delivery of curcumin into these cells when in the form of CurNPs compared to its free form. A hydrogen peroxide-based oxidative stress study also demonstrated the CurNP’s potential to protect J774 A.1 cells against excessive oxidative stress. Overall, this study provides evidence for the suitability of CurNPs to be used as a bioactive agent in NC applications.

Advancements in Thermal Insulation through Ceramic Micro-Nanofiber Materials

Ceramic fibers have the advantages of high temperature resistance, light weight, favorable chemical stability and superior mechanical vibration resistance, which make them widely used in aerospace, energy, metallurgy, construction, personal protection and other thermal protection fields. Further refinement of the diameter of conventional ceramic fibers to microns or nanometers could further improve their thermal insulation performance and realize the transition from brittleness to flexibility. Processing traditional two-dimensional (2D) ceramic fiber membranes into three-dimensional (3D) ceramic fiber aerogels could further increase porosity, reduce bulk density, and reduce solid heat conduction, thereby improving thermal insulation performance and expanding application areas. Here, a comprehensive review of the newly emerging 2D ceramic micro-nanofiber membranes and 3D ceramic micro-nanofiber aerogels is demonstrated, starting from the presentation of the thermal insulation mechanism of ceramic fibers, followed by the summary of 2D ceramic micro-nanofiber membranes according to different types, and then the generalization of the construction strategies for 3D ceramic micro-nanofiber aerogels. Finally, the current challenges, possible solutions, and future prospects of ceramic micro-nanofiber materials are comprehensively discussed. We anticipate that this review could provide some valuable insights for the future development of ceramic micro-nanofiber materials for high temperature thermal insulation.

Development and preparation of novel nano-enhanced organic eutectic phase change materials for low-temperature solar thermal applications

ABSTRACT Thermally reliable and stable eco-friendly Phase change materials are of significant aid in thermal energy storage technology, leading to improved energy utilization and reliability of the system. This study develops two novel organic eutectic PCM of Lauric acid – Margaric acid (LM) and Myristic acid – Margaric acid (MM), which are chemically stable and thermally compatible for latent heat energy storage. LM eutectic mixture had a melting temperature of 52.66°C with a latent heat of 163.68 J/g, and MM eutectic mixture had its melting temperature at 44.79°C and a latent heat of 197.31 J/g. The phase change temperatures were favorable for low temperature solar thermal applications with good latent heat capacity. The thermal characteristics of these eutectic mixtures are further enhanced with the dispersion of highly conductive Multi walled carbon nanotubes (MWCNT) at three different mass fractions (.5%, 1% and 1.5% by weight). Nano enhancement could achieve exceptional thermal conductivity enhancement in MM eutectic mixture by 110.6% and 83.73% in LM eutectic mixture. Thermogravimetric analysis and Fourier-transform infrared spectroscopy analysis ensured the thermal and chemical stability of the eutectic mixtures. The optical absorption characteristics were extensively enhanced with nano particle addition, which is highly preferable in solar thermal applications.

Advanced Hierarchical Biomorphous Silicon Carbide Monoliths

Porous silicon carbide (SiC) has attracted considerable attention in the field of cellular ceramics for a variety of applications such as catalyst supports, filters, or in the biomedical field due to its excellent structural properties, mechanical strength, and chemical stability. However, SiC has certain limitations due to high‐temperature profiles and costly manufacturing methods. Therefore, it is investigated that porous biomorphic silicon carbide monoliths using a powder blend of paper‐derived carbon fibers, phenolic resin, and silicon, resulting in comparatively low sintering temperatures (T = 1300 to 1550 °C) and good mechanical strength. This near‐net‐shape process uses low‐cost raw materials and enables the production of silicon carbides with high open porosity (P = 51.48% to 68.28%) and low shrinkage. The influence of different amounts of carbon sources (Cfibers and Cresin) on the mechanical (4‐point bending) and thermal properties (laser flash method) is investigated. In addition, to improve the pressure gradients, macrochannels with multiple layers of sacrificial polymer lattices are incorporated, resulting in hierarchical structures with high permeability. Thus, this advanced biomimetic approach offers great potential for structured cellular ceramics with tailored properties for biomedical, catalyst support, or nuclear fuel cladding materials.

Synthesis of High‐Sodium‐Content Oxythiosilicate Glass Electrolytes Via Sodium Polysulfide

AbstractSulfide glass electrolytes with high ionic conductivities and formabilities are key materials for practical use in all‐solid‐state sodium secondary batteries. Both sealing and quenching are considered to be necessary for producing high‐alkali‐content sulfide glass electrolytes. In this study, the glass‐forming ability of sodium thiosilicate glasses is enhanced by adding a small quantity of SiO2. Consequently, high‐sodium‐content oxythiosilicate glass is synthesized without sealing and quenching processes under Ar atmosphere. The prepared Na4SiS4·0.200SiO2 (molar ratio) glass exhibits ionic conductivity of 4.0 × 10−5 S cm−1 at 25 °C, surpassing that of Na4SiS4 glass. The Na4SiS4·0.200SiO2 glass shows high reduction stability to sodium metal. The all‐solid‐state Na metal/Na4SiS4·0.200SiO2 glass/Na2.88Sb0.88W0.12S4/TiS2 cell shows a reversible capacity of 140 mAh g−1 for 5 cycles. The amount of H2S gas generated in Na4SiS4·0.0830SiO2 and Na4SiS4·0.200SiO2 glasses is one‐tenth that of the Na4SiS4 glass, suggesting increased chemical stability to humidity by incorporating oxygen in the structure. High‐sodium‐content oxythiosilicate glass with high ionic conductivity, high chemical stability against humidity, and high reduction stability is successfully prepared under ambient pressure without sealing and quenching processes.

Scalable Synthesis of SiOx-TiON Composite As an Ultrastable Anode for Li-Ion Half/Full Batteries.

Among various anode materials, SiOx is regarded as the next generation of promising anode due to its advantages of high theoretical capacity with 2680 mA h g-1, low lithium voltage platform, and rich natural resources. However, the pure SiOx-based materials have slow lithium storage kinetics attributed to their low electron/ion conductive properties and the large volume change during lithiation/delithiation, restricting their practical application. Optimizing the SiOx material structures and the fabricating methods to mitigate these fatal defects and adapt to the market demand for energy density is critical. Hence, SiOx material with TiO1-xNx phase modification has been prepared by simple, low-cost, and scalable ball milling and then combined with nitridation. Consequently, based on the TiO1-xNx modified layer, which boosts high ionic/electronic conductivity, chemical stability, and excellent mechanical properties, the SiOx@TON-10 electrode shows highly stable lithium-ion storage performance for lithium-ion half/full batteries due to a stable solid-electrolyte interface layer, fast Li+ transport channel, and alleviative volumetric expansion, further verifying its practical feasibility and universal applicability.

Two-dimensional metal–organic framework for post-synthetic immobilization of graphene quantum dots for photoluminescent sensing

Immobilization of graphene quantum dots (GQDs) on a solid support is crucial to prevent GQDs from aggregation in the form of solid powder and facilitate the separation and recycling of GQDs after use. Herein, spatially dispersed GQDs are post-synthetically coordinated within a two-dimensional (2D) and water-stable zirconium-based metal–organic framework (MOF). Unlike pristine GQDs, the obtained GQDs immobilized on 2D MOF sheets show photoluminescence in both suspension and dry powder. Chemical and photoluminescent stabilities of MOF-immobilized GQDs in water are investigated, and the use of immobilized GQDs in the photoluminescent detection of copper ions is demonstrated. Findings here shed the light on the use of 2D MOFs as a platform to further immobilize GQDs with various sizes and distinct chemical functionalities for a range of applications.

Ceramic-Based Dielectric Materials for Energy Storage Capacitor Applications

Materials offering high energy density are currently desired to meet the increasing demand for energy storage applications, such as pulsed power devices, electric vehicles, high-frequency inverters, and so on. Particularly, ceramic-based dielectric materials have received significant attention for energy storage capacitor applications due to their outstanding properties of high power density, fast charge–discharge capabilities, and excellent temperature stability relative to batteries, electrochemical capacitors, and dielectric polymers. In this paper, we present fundamental concepts for energy storage in dielectrics, key parameters, and influence factors to enhance the energy storage performance, and we also summarize the recent progress of dielectrics, such as bulk ceramics (linear dielectrics, ferroelectrics, relaxor ferroelectrics, and anti-ferroelectrics), ceramic films, and multilayer ceramic capacitors. In addition, various strategies, such as chemical modification, grain refinement/microstructure, defect engineering, phase, local structure, domain evolution, layer thickness, stability, and electrical homogeneity, are focused on the structure–property relationship on the multiscale, which has been thoroughly addressed. Moreover, this review addresses the challenges and opportunities for future dielectric materials in energy storage capacitor applications. Overall, this review provides readers with a deeper understanding of the chemical composition, physical properties, and energy storage performance in this field of energy storage ceramic materials.

Microstructure and performance modification of PVDF ultrafiltration membrane via adjusting the composition of coagulation Bath

AbstractIn this paper, the effect of the composition of a nonsolvent bath on the physicochemical properties of the polyvinylidene fluoride (PVDF) ultrafiltration membranes were comprehensively investigated using the nonsolvent‐induced phase separation method. Three additives (ethanol, glycerol, or NaCl) were added to the water coagulation bath respectively to obtain different membranes. It was found that the microstructure of the membranes changed from finger‐like structure to the sponge‐like structure with the increase of additives concentration, which successfully improved the retention and mechanical properties of the membranes. In addition, the membrane surface became smoother and more hydrophilic. The membrane fabricated in 30 wt% glycerol bath exhibited outstanding comprehensive properties of retention and anti‐fouling, with a water flux of 243.5 L/(m2 h), a bovine serum albumin rejection of more than 90%, and a flux recovery rate of 97%. From mechanism analysis, the addition of ethanol, glycerol, or NaCl to the coagulation bath altered the thermodynamic stability of the polymer system, and slowed down the rate of solvent and nonsolvent diffusion from a kinetic perspective. This research provides important clues for optimizing the membrane properties, such as flux, rejection, and strength.

Investigation of Phase Transformations and Ordering Mechanisms in a Pd–Cu–Ag–Ru Alloy

An in‐depth analysis of phase transformations in a Pd–Cu–Ag alloy, crucial for applications in hydrogen membranes and electrical components, is presented. The investigation emphasizes the influence of the deformation rate and addition of Ag on the formation of the ordered CuPd phase. This study focuses on a specific alloy composition, 49.1% Cu–41.3% Pd–8.3% Ag–1.3% Ru, investigating its behavior under various conditions. Through comprehensive analysis, including the influence of the initial state, deformation variations, and chemical composition modifications, high‐energy X‐ray diffraction to unveil detailed phase evolution dynamics is used. Surprisingly, experimental findings deviate from the anticipated phase diagram, uncovering a previously unrecognized three‐phase region with the formation of AgPd. Notably, the study reveals the pivotal role of the alloy's Ag content in the development of ordered CuPd and AgPd phases. The addition of Ru exhibits no involvement in the observed phase transformations, contributing to the understanding of the alloy's composition‐dependent behavior. This research provides valuable insights into the intricate interplay of factors influencing phase transformations, offering a nuanced perspective beyond theoretical predictions. The newfound understanding of Ag's role and Ru's inertness refines material design considerations, enhancing the grasp of the alloy's thermodynamic stability under varying conditions.